Durethan® DP BM 410 H2.0|PA6-(GF+MD)10|LANXESS物性表报告及物性特性介绍,Durethan® DP BM 410 H2.0|PA6-(GF+MD)10|LANXESS注塑参数详情-塑料物性表查询网

0 | PA6-(GF+MD)10 |LANXESS Product TextsPA 6, 10 % mineral, injection moulding, heat-ageing stabilized

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	36 / *	cm³/10min	ISO 1133
温度(Temperature)	270 / *	°C	ISO 1133
负载(Load)	2.16 / *	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	1.2 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.0 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	4060 / 1340	MPa	ISO 527-1/-2
屈服应力(Yield stress)	80 / 40	MPa	ISO 527-1/-2
屈服应变(Yield strain)	3.5 / 22.6	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	65 / N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	50 / N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	10 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	68 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	182 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	70 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	90 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相比漏电起痕指数(Comparative tracking index)	500 / -	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸湿性(Humidity absorption)	2.5 / *	%	Sim. to ISO 62
密度(Density)	1210 / -	kg/m³	ISO 1183

CharacteristicsProcessingInjection MoldingDelivery formPelletsRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING Water content: 0.1 % .