Orgalloy® LE 6000|PA6...|ARKEMA 物性表: Orgalloy® LE 6000|PA6...|ARKEMA物性表及特性介绍,Orgalloy® LE 6000|PA6...|ARKEMA注塑参数详情,如需Orgalloy® LE 6000|PA6...|ARKEMA下载, 可到相关下载区下载

.. |ARKEMA Product TextsAlso suited to injection 16 / *		kgISO 1133
成型收缩(Molding shrinkage) (parallel)0.8 / *%ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)0.7 / *%ISO 294-4, 2577
机械性能(机械性能(Mechanical properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)1820 / 1400MPaISO 527-1/-2
屈服应力(Yield stress)44 / 36MPaISO 527-1/-2
屈服应变(Yield strain)4 / 7%ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)>50 / >50%ISO 527-1/-2
Tensile creep modulus (1h)* / 1130MPaISO 899-1
Tensile creep modulus (1000h)* / 520MPaISO 899-1
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)29 / 35kJ/m²ISO 179/1eA
Shore D hardness (15s)66 / *-ISO 868
热性能(热性能(Thermal properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)220 / *°CISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)45 / *°CISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature118 / *°CISO 306
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.HB / *classIEC 60695-11-10
厚度测试(Thickness tested)1.6 / *mmIEC 60695-11-10
UL 识别(recognition)UL / *--
燃烧性(球压痕硬度(Burning behav)). at thickness hHB / *classIEC 60695-11-10
厚度测试(Thickness tested)3.2 / *mmIEC 60695-11-10
UL 识别(recognition)UL / *--
电气性能(Electrical properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相比漏电起痕指数(Comparative tracking index)* / 600-IEC 60112
其他属性(Other properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)6.4 / *%Sim. to ISO 62
吸湿性(Humidity absorption)1.8 / *%Sim. to ISO 62
密度(Density)1040 / 1040kg/m³ISO 1183
Film Propertiesdry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Stress at yield (parallel)25 / *MPaISO 527-3
Stress at yield (normal)26 / *MPaISO 527-3
Strain at yield (parallel)20 / *%ISO 527-3
Strain at yield (normal)14 / *%ISO 527-3
Maximum stress (parallel)53 / *MPaISO 527-3
Maximum stress (normal)41 / *MPaISO 527-3
Maximum strain (parallel)410 / *%ISO 527-3
Maximum strain (normal)490 / *%ISO 527-3
Elmendorf Tear resistance (parallel)25 / *NISO 6383-2
Elmendorf Tear resistance (normal)150 / *NISO 6383-2
Dart drop B313 / *gISO 7765-1
WVTR (23°C/85%r.h.)60 / *g/(m²*d)DIS 15106-1/-2
Oxygen transmission rate (23°C/0%r.h.)90 / *cm³/(m²*d*bar)DIS 15105-1/-2
Oxygen transmission rate (23°C/85%r.h.)90 / *cm³/(m²*d*bar)DIS 15105-1/-2
Carbon Dioxide transm. rate (23°C/0%r.h.)290 / *cm³/(m²*d*bar)DIS 15105-1/-2
Carbon Dioxide transm. rate (23°C/85%r.h.)290 / *cm³/(m²*d*bar)DIS 15105-1/-2
Test specimen production值(Value)单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature260°CISO 294
Injection Molding, mold temperature60°CISO 10724
Diagrams ISO 1817 Liquid 4) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .
[/td][/tr][/table]

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/wuxingbiao/show-93578.html

免责声明: 本文 Orgalloy® LE 6000|PA6...|ARKEMA 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4