Technyl® C 52G1 V20|PA6-GF20|Rhodia物性表报告及物性特性介绍,Technyl® C 52G1 V20|PA6-GF20|Rhodia注塑参数详情-塑料物性表查询网

Technyl® C 52G1 V20|PA6-GF20|Rhodia

Product Texts Polyamide6, 20% Glass-fiber reinforced, glow-wire modified, lubricated for injection moulding9 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.7 / *	%	ISO 294-4, 2577

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	222 / *	°C	ISO 11357-1/-3
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相比漏电起痕指数(Comparative tracking index)	500 / -	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.2 / *	%	Sim. to ISO 62
密度(Density)	1340 / -	kg/m³	ISO 1183

Diagrams In the case that the virgin material has absorbed moisture, it must be dried to a final moisture content less than 0.2% with a dehumidified air drying equipment at approx.80°C .
[/td][/tr][/table]