Technyl® eXten D 458P|PA610-I|Rhodia物性表报告及物性特性介绍,Technyl® eXten D 458P|PA610-I|Rhodia注塑参数详情-塑料物性表查询网

Product TextsHigh viscosity unfilled plasticized PA6.10 for extrusion applications providing low end part warpage.

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
成型收缩(Molding shrinkage) (parallel)	3.5 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	3.0 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	800 / 550	MPa	ISO 527-1/-2
Stress at 50% strain	40 / 34	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	>50 / >50	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N / N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N / N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	87 / 117	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	15 / 19	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	215 / *	°C	ISO 11357-1/-3
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.6 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.5 / *	%	Sim. to ISO 62
密度(Density)	1040 / -	kg/m³	ISO 1183

CharacteristicsSpecial CharacteristicsHigh impact or impact modifiedRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingThe material is supplied in airtight bags, ready fro use. In the case that the virgin material has absorbedmoisture, it must be dried to a final moisture content less than 0,1% with a dehumidified air drying equipment at approximately 80°C. ISO 1817 Liquid 4) (23°C)