Ultramid® TG7S BK-102|PA6-GF35|BASF物性表报告及物性特性介绍,Ultramid® TG7S BK-102|PA6-GF35|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® TG7S is a 34% glass reinforced, heat stabilized, impact modified Polyamid 6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to bemade of an engineering plastic as opposed to metal. This material passed the Key end-use submarine impact test for General Motors H-Car Seat Pan Frame. TG7S exhibits improved strength, stiffness and notched impact properties over Ultramid® 8333G HI, at a significantly lower costThis material is also available in black.

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	6 / *	cm³/10min	ISO 1133
温度(Temperature)	235 / *	°C	ISO 1133
负载(Load)	5 / *	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	9500 / -	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	165 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2.5 / -	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	22 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	208 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	220 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1370 / -	kg/m³	ISO 1183

Diagrams Water content: 0.08% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rate.DisclaimerCopyright M-Base .