Ultramid® HMG13 HS BK-102|PA6-GF63|BASF物性表报告及物性特性介绍,Ultramid® HMG13 HS BK-102|PA6-GF63|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus Polyamid designed to have high strength and stiffness for metal replacement applications.It also has excellent moldability and outstanding surface appearance.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	22400 / 13400	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	245 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2 / -	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	214 / *	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1740 / -	kg/m³	ISO 1183

Diagrams Water content: 0.03% A dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rate.DisclaimerCopyright M-Base .