Rynite® 935 NC010|PET-(MD+GF)35|DuPont物性表报告及物性特性介绍,Rynite® 935 NC010|PET-(MD+GF)35|DuPont注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	5	cm³/10min	ISO 1133
温度(Temperature)	280	°C	ISO 1133
负载(Load)	5	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.3	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.7	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	10000	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	85	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	2	%	ISO 527-1/-2
Tensile creep modulus (1h)	9400	MPa	ISO 899-1
Tensile creep modulus (1000h)	7700	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	25	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	20	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	6	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	4	kJ/m²	ISO 179/1eA
Puncture - maximum force (+23°C)	780	N	ISO 6603-2
Puncture energy (+23°C)	2.7	J	ISO 6603-2
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	9930.02	MPa	ASTM D 638
抗拉强度(Tensile Strength)	89.6	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	2	%	ASTM D 638
抗压强度(Compressive Strength)	141	MPa	ASTM D 695
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	9599.97	MPa	ASTM D 790
抗弯强度(Flexural Strength)	141	MPa	ASTM D 790
洛氏硬度(Rockwell Hardness)	R 115	-	ASTM D 785
悬臂梁式冲击切口 (1/8 in)	0.064	kJ/m	ASTM D 256
悬臂梁式冲击切口 (Low-温度(Temperature))	0.043	kJ/m	ASTM D 256
温度(Temperature)	-40	°C	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	252	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	200	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	235	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	205	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	20	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	50	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
UL 识别(recognition)	UL	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10
UL 识别(recognition)	UL	-	-
Oxygen index	21	%	ISO 4589-1/-2
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	HB	-	UL 94
厚度测试(Thickness tested)	0.75	mm	-
热膨胀系数(Coefficient of Thermal Expansion) (MD)	16	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	52	E-6/K	ASTM D 696
DTUL @ 66 psi	241	°C	ASTM D 648
DTUL @ 264 psi	215	°C	ASTM D 648
熔化温度(Melting 温度(Temperature))	252	°C	ASTM D 3418

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	4.5	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	4.1	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	300	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	200	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E14	Ohm	IEC 60093
电气强度(Electric strength)	39	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	300	-	IEC 60112
ASTM数据(ASTM Data)
绝缘强度(Dielectric Strength) (Short Time)	23.5	kV/mm	ASTM D 149
耗散因数(Dissipation Factor) (1 MHz)	0.01	-	ASTM D 150
介电常数(Dielectric Constant) (1 MHz)	3.7	-	ASTM D 150
表面电阻率(Surface Resistivity)	1E14	Ohm	ASTM D 257
体积电阻率(Volume Resistivity)	1E15	Ohm*cm	ASTM D 257

Diagrams ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (90°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)