EMERGE™ PC 8310-10 (EU)|PC|Styron物性表报告及物性特性介绍,EMERGE™ PC 8310-10 (EU)|PC|Styron注塑参数详情-塑料物性表查询网

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577
熔体流动指数(熔体流动指数(Melt flow index)) (MFI)	10	g/10min	ISO 1133
MFI温度(MFI temperature)	300	°C	ISO 1133
MFI负载(MFI load)	1.2	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2400	MPa	ISO 527-1/-2
屈服应力(Yield stress)	60	MPa	ISO 527-1/-2
屈服应变(Yield strain)	6	%	ISO 527-1/-2
破坏时应变(Stress at break)	58	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	>50	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	35	kJ/m²	ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)	2350	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	70	kJ/m²	ISO 180/1A

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	123	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	143	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	70	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	V-2	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
Oxygen index	40	%	ISO 4589-1/-2
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	V-0	-	UL 94
厚度测试(Thickness tested)	3	mm	-

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
体积电阻率(Volume resistivity)	1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	1E15	Ohm	IEC 60093
电气强度(Electric strength)	17	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	225	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
密度(Density)	1200	kg/m³	ISO 1183

Optical properties	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
Light Transmittance	89	%	ASTM D 1003

CharacteristicsProcessingInjection MoldingAdditivesRelease agentSpecial CharacteristicsHeat stabilized or stable to heat, TransparentApplicationsIT / Business Machine, Electrical and ElectronicalRegional AvailabilityEurope, Near East/AfricaDisclaimerCopyright M-Base .