Lexan ML7677A|PC|沙特基础 物性表: Lexan ML7677A|PC|沙特基础物性表及特性介绍,Lexan ML7677A|PC|沙特基础注塑参数详情,如需Lexan ML7677A|PC|沙特基础下载, 可到相关下载区下载

加工/物理特性值(Value)单位(Unit)测试标准(Test Standard)
ASTM数据(ASTM Data)
熔体流动指数(Melt Flow Index)23g/10minASTM D 1238
温度(Temperature)260°C-
负载(Load)2.16kg-
模具收缩(Mold Shrinkage) (MD)0.007mm/mmASTM D 955
模具收缩(Mold Shrinkage) (TD)0.007mm/mmASTM D 955
密度(Density) (73°F)1230kg/m³ASTM D 792
流变性能(Rheological properties)值(Value)单位(Unit)测试标准(Test Standard)
ISO数据
熔体体积流动速率(Melt volume-flow rate) (MVR)43cm³/10minISO 1133
温度(Temperature)300°CISO 1133
负载(Load)1.2kgISO 1133
机械性能(机械性能(Mechanical properties))值(Value)单位(Unit)测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)2650MPaISO 527-1/-2
屈服应力(Yield stress)70MPaISO 527-1/-2
屈服应变(Yield strain)5%ISO 527-1/-2
破坏时应变(Stress at break)54MPaISO 527-1/-2
破坏时应变(Strain at break)>50%ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)131kJ/m²ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)130kJ/m²ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)4kJ/m²ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)4kJ/m²ISO 179/1eA
弯曲弹性模量(Flexural modulus) (23°C)2600MPaISO 178
悬臂梁式冲击切口 (23°C)4kJ/m²ISO 180/1A
悬臂梁式冲击切口4kJ/m²ISO 180/1A
温度(Temperature)-30°CISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)182kJ/m²ISO 180/1U
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)2670MPaASTM D 638
抗拉强度(Tensile Strength) at Yield69MPaASTM D 638
抗拉强度(Tensile Strength) at Break52MPaASTM D 638
屈服伸长率(Elongation at Yield)5%ASTM D 638
断裂伸长率(Elongation at Break)50%ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))2300MPaASTM D 790
悬臂梁式冲击切口 (1/8 in)0.0384kJ/mASTM D 256
悬臂梁式冲击切口 (Low-温度(Temperature))0.0356kJ/mASTM D 256
温度(Temperature)-30°CASTM D 256
热性能(热性能(Thermal properties))值(Value)单位(Unit)测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)97°CISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature111°CISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)72E-6/KISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)74E-6/KISO 11359-1/-2
燃烧性厚度(Burning behav. at thickness h)V-1classIEC 60695-11-10
厚度测试(Thickness tested)2.0mmIEC 60695-11-10
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)65E-6/KASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)66E-6/KASTM D 696
DTUL @ 264 psi94°CASTM D 648
Vicat 温度(Temperature)114°CASTM D 1525
其他属性(Other properties)值(Value)单位(Unit)测试标准(Test Standard)
ISO数据
吸水率(Water absorption)0.28%Sim. to ISO 62
吸湿性(Humidity absorption)0.35%Sim. to ISO 62
密度(Density)1230kg/m³ISO 1183
ColorSpecial CharacteristicsFlame retardantRegional Availability .

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/wuxingbiao/show-97798.html

免责声明: 本文 Lexan ML7677A|PC|沙特基础 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4