Makrolon® FR7087|PC FR|Bayer MatSc物性表报告及物性特性介绍,Makrolon® FR7087|PC FR|Bayer MatSc注塑参数详情-塑料物性表查询网

Product TextsMVR (300 °C/1.2 kg) 12 cm3/10 minflame retardantUL 94V-0/2.2 mm and 5VA/3.0 mmmedium viscosityUV stabilizedeasy releaseavailable in transparent and translucent colorselectrical/electronic

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	12	cm³/10min	ISO 1133
温度(Temperature)	300	°C	ISO 1133
负载(Load)	1.2	kg	ISO 1133

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2500	MPa	ISO 527-1/-2
屈服应力(Yield stress)	75	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N	kJ/m²	ISO 179/1eU

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	106	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	118	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-2	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
UL 识别(recognition)	UL	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	2.2	mm	IEC 60695-11-10
UL 识别(recognition)	UL	-	-
燃烧性(球压痕硬度(Burning behav)). 5V at thickness h	5VA	class	IEC 60695-11-20
厚度测试(Thickness tested)	3.0	mm	IEC 60695-11-20
UL 识别(recognition)	UL	-	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentSpecial CharacteristicsFlame retardant, Light stabilized or stable to light, U.V. stabilized or stable to weatherRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING Water content: 0.02 % .