XANTAR® LDS 3750|PC FR...|Mitsubishi EP物性表报告及物性特性介绍,XANTAR® LDS 3750|PC FR...|Mitsubishi EP注塑参数详情-塑料物性表查询网

.. |Mitsubishi EP Product TextsLaser Direct Structuring (LDS) *, Low Viscosity, Flame Retardant (Halogen free), Black color only.. Please address straight to LPKF Laser & Electronics AG (www.LPKF.de).

流变性能(Rheological properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	14	cm³/10min	ISO 1133
温度(Temperature)	300	°C	ISO 1133
负载(Load)	1.2	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2300	MPa	ISO 527-1/-2
屈服应力(Yield stress)	60	MPa	ISO 527-1/-2
屈服应变(Yield strain)	6	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2
Puncture energy (+23°C)	40	J	ISO 6603-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	126	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	145	°C	ISO 306
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-0	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8	mm	IEC 60695-11-10

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.35	%	Sim. to ISO 62
密度(Density)	1260	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	280	°C	ISO 294
Injection Molding, mold temperature	100	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsAdditivesRelease agentSpecial CharacteristicsFlame retardant, PlatableRegional AvailabilityEurope, Asia PacificOther text informationInjection moldingInjection Molding RecommendationsDisclaimerCopyright M-Base .