- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.64
- 弯曲强度 [MPa]: 79.0
- 热变形温度 [℃]: 99.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
Water Absorption | 0.25 % | 0.25 % | 24 hrs. ASTM D570 |
Linear Mold Shrinkage | 0.0025 - 0.0040 cm/cm @Thickness 3.17 mm | 0.0025 - 0.0040 in/in @Thickness 0.125 in | ASTM D955 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 79.0 MPa | 11500 psi | ASTM D638 |
Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
Tensile Modulus | 5.90 GPa | 856 ksi | ASTM D638 |
Izod Impact, Notched | 0.640 J/cm @Thickness 6.35 mm | 1.20 ft-lb/in @Thickness 0.250 in | ASTM D256 |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 10000 - 1.00e+6 ohm-cm | 10000 - 1.00e+6 ohm-cm | ASTM D257 |
Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Thermal Properties | Metric | English | Comments |
Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
Processing Properties | Metric | English | Comments |
Melt Temperature | 221 - 249 °C | 430 - 480 °F | Stock |
Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
Drying Temperature | 77.0 °C | 171 °F |