- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.69
- 弯曲强度 [MPa]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM D638 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 6.35 mm | 1.29 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+9 - 1.00e+13 ohm | 1.00e+9 - 1.00e+13 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 221 - 243 °C | 430 - 469 °F | Stock |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |