- 熔体流动速率 [g/10min]: 0.19
- 密度 [g/cm3]: 0.921
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 3.4
- 弯曲强度 [MPa]: 3.4
- 弯曲模量 [MPa]: 0.0190
- 脆化温度 [℃]: -90.0
- 透光率 [%]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 - 0.970 g/cc | 0.0333 - 0.0350 lb/in³ | Average value: 0.931 g/cc Grade Count:192 |
| Water Absorption | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:3 |
| Moisture Vapor Transmission | 0.590 - 0.940 cc-mm/m²-24hr-atm | 1.50 - 2.39 cc-mil/100 in²-24hr-atm | Average value: 0.789 cc-mm/m²-24hr-atm Grade Count:8 |
| Water Vapor Transmission | 85.3 g/m²/day | 5.49 g/100 in²/day | Average value: 85.3 g/m²/day Grade Count:3 |
| Oxygen Transmission | 158 - 229 cc-mm/m²-24hr-atm | 401 - 582 cc-mil/100 in²-24hr-atm | Average value: 199 cc-mm/m²-24hr-atm Grade Count:8 |
| Oxygen Transmission Rate | 8900 cc/m²/day | 573 cc/100 in²/day | Average value: 8900 cc/m²/day Grade Count:3 |
| Viscosity | 2.00e+6 - 2.00e+6 cP @Temperature 190 - 190 °C | 2.00e+6 - 2.00e+6 cP @Temperature 374 - 374 °F | Average value: 2.00e+6 cP Grade Count:2 |
| 2.00e+6 - 2.00e+6 cP @Shear Rate 50.0 - 50.0 1/s | 2.00e+6 - 2.00e+6 cP @Shear Rate 50.0 - 50.0 1/s | Average value: 2.00e+6 cP Grade Count:2 | |
| Environmental Stress Crack Resistance | 500 hour | 500 hour | Average value: 500 hour Grade Count:16 |
| Vinyl Acetate Content | 2.00 - 29.5 % | 2.00 - 29.5 % | Average value: 10.5 % Grade Count:83 |
| Thickness | 15.0 - 300 microns | 0.591 - 11.8 mil | Average value: 52.6 microns Grade Count:110 |
| Melt Flow | 0.190 - 135 g/10 min | 0.190 - 135 g/10 min | Average value: 2.75 g/10 min Grade Count:197 |
| Antiblock Level | 0.000 - 15000 ppm | 0.000 - 15000 ppm | Average value: 4280 ppm Grade Count:22 |
| Slip Level | 0.000 - 7050 ppm | 0.000 - 7050 ppm | Average value: 1150 ppm Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72.0 - 96.0 | 72.0 - 96.0 | Average value: 86.3 Grade Count:28 |
| Hardness, Shore D | 23.0 - 94.0 | 23.0 - 94.0 | Average value: 41.9 Grade Count:54 |
| Tensile Strength, Ultimate | 3.40 - 33.0 MPa | 493 - 4790 psi | Average value: 15.2 MPa Grade Count:52 |
| Film Tensile Strength at Yield, MD | 3.00 - 15.0 MPa | 435 - 2180 psi | Average value: 7.43 MPa Grade Count:86 |
| Film Tensile Strength at Yield, TD | 2.00 - 11.0 MPa | 290 - 1600 psi | Average value: 6.71 MPa Grade Count:86 |
| Tensile Strength, Yield | 3.40 - 10.0 MPa | 493 - 1450 psi | Average value: 8.00 MPa Grade Count:45 |
| Film Elongation at Break, MD | 100 - 620 % | 100 - 620 % | Average value: 333 % Grade Count:145 |
| Film Elongation at Break, TD | 260 - 950 % | 260 - 950 % | Average value: 589 % Grade Count:145 |
| Film Elongation at Yield, MD | 6.40 - 19.4 % | 6.40 - 19.4 % | Average value: 9.03 % Grade Count:24 |
| Film Elongation at Yield, TD | 5.40 - 16.0 % | 5.40 - 16.0 % | Average value: 7.38 % Grade Count:24 |
| Elongation at Break | 50.0 - 1200 % | 50.0 - 1200 % | Average value: 564 % Grade Count:69 |
| Modulus of Elasticity | 0.00500 - 0.338 GPa | 0.725 - 49.0 ksi | Average value: 0.159 GPa Grade Count:54 |
| Flexural Modulus | 0.0190 - 0.0960 GPa | 2.76 - 13.9 ksi | Average value: 0.0561 GPa Grade Count:15 |
| Secant Modulus | 0.0531 - 1.05 GPa | 7.70 - 152 ksi | Average value: 0.601 GPa Grade Count:6 |
| Secant Modulus, MD | 0.0241 - 0.400 GPa | 3.50 - 58.0 ksi | Average value: 0.124 GPa Grade Count:123 |
| Secant Modulus, TD | 0.0248 - 0.800 GPa | 3.60 - 116 ksi | Average value: 0.146 GPa Grade Count:123 |
| Tensile Impact Strength | 146 - 815 kJ/m² | 69.5 - 388 ft-lb/in² | Average value: 596 kJ/m² Grade Count:16 |
| Coefficient of Friction | 0.100 - 3.40 | 0.100 - 3.40 | Average value: 0.547 Grade Count:24 |
| Elmendorf Tear Strength MD | 40.0 - 600 g | 40.0 - 600 g | Average value: 217 g Grade Count:56 |
| Elmendorf Tear Strength TD | 30.0 - 345 g | 30.0 - 345 g | Average value: 131 g Grade Count:56 |
| Elmendorf Tear Strength, MD | 0.197 - 18.9 g/micron | 5.00 - 480 g/mil | Average value: 5.00 g/micron Grade Count:75 |
| Elmendorf Tear Strength, TD | 0.945 - 9.06 g/micron | 24.0 - 230 g/mil | Average value: 3.59 g/micron Grade Count:68 |
| Dart Drop | 1.97 - 30.0 g/micron | 50.0 - 762 g/mil | Average value: 6.89 g/micron Grade Count:117 |
| Dart drop Test | 70.0 - 700 g | 0.154 - 1.54 lb | Average value: 270 g Grade Count:97 |
| Film Tensile Strength at Break, MD | 15.0 - 40.0 MPa | 2180 - 5800 psi | Average value: 27.1 MPa Grade Count:146 |
| Film Tensile Strength at Break, TD | 13.0 - 40.0 MPa | 1890 - 5800 psi | Average value: 24.4 MPa Grade Count:139 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 - 1.00e+15 ohm-cm | 1.00e+14 - 1.00e+15 ohm-cm | Average value: 3.25e+14 ohm-cm Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | -7.78 - 110 °C | 18.0 - 230 °F | Average value: 93.4 °C Grade Count:143 |
| Crystallization Temperature | 85.0 - 96.0 °C | 185 - 205 °F | Average value: 90.9 °C Grade Count:16 |
| Vicat Softening Point | 44.0 - 96.0 °C | 111 - 205 °F | Average value: 78.2 °C Grade Count:144 |
| Brittleness Temperature | -90.0 - -76.0 °C | -130 - -105 °F | Average value: -79.6 °C Grade Count:18 |
| Shrinkage | 0.000 - 4.00 % @Temperature 120 - 120 °C | 0.000 - 4.00 % @Temperature 248 - 248 °F | Average value: 0.750 % Grade Count:3 |
| 0.000 - 4.00 % @Time 180 - 180 sec | 0.000 - 4.00 % @Time 0.0500 - 0.0500 hour | Average value: 0.750 % Grade Count:3 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | Average value: 1.49 Grade Count:3 |
| Haze | 1.00 - 28.0 % | 1.00 - 28.0 % | Average value: 6.74 % Grade Count:154 |
| Gloss | 17.0 - 123 % | 17.0 - 123 % | Average value: 71.2 % Grade Count:145 |
| Yellow Index | 2.90 - 8.20 % | 2.90 - 8.20 % | Average value: 5.71 % Grade Count:3 |
| Transmission, Visible | 10.0 - 90.0 % | 10.0 - 90.0 % | Average value: 85.4 % Grade Count:56 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 140 - 210 °C | 284 - 410 °F | Average value: 170 °C Grade Count:11 |
| Melt Temperature | 65.0 - 221 °C | 149 - 430 °F | Average value: 180 °C Grade Count:61 |
| Die Opening | 0.0635 - 0.150 cm | 0.0250 - 0.0591 in | Average value: 0.0812 cm Grade Count:9 |
| Blow-up Ratio (BUR) | 2.00 - 3.00 | 2.00 - 3.00 | Average value: 2.21 Grade Count:29 |
| Gel Time | 0.000 - 20.0 min @Temperature 135 - 155 °C | 0.000 - 20.0 min @Temperature 275 - 311 °F | Average value: 8.81 min Grade Count:2 |