- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 7.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | |
| Melt Flow | 0.45 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.45 g/10 min @Load 4.76 lb, Temperature 374 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.100 GPa | 14.5 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 93.0 °C | 199 °F | 10°C/min |
| Vicat Softening Point | 74.0 °C | 165 °F | 50°C/hr; 50N |