- 熔体流动速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 6.0 % | 6.0 % | |
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | ASTM D1238 Cond. E |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 360 % | 360 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Secant Modulus, MD | 0.120 GPa | 17.4 ksi | ASTM D882 |
| Secant Modulus, TD | 0.125 GPa | 18.1 ksi | ASTM D882 |
| Coefficient of Friction | 0.15 | 0.15 | ASTM D1894 |
| Dart drop Test | 85.0 g | 0.187 lb | Thickness not specified @ 50% Fail, ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D2457 |
| Gloss | 64 % | 64 % | 45° Gloss, ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 210 °C | 320 - 410 °F | |