- 熔体流动速率 [g/10min]: 1.6
- 密度 [g/cm3]: 0.937
- 弯曲模量 [MPa]: 0.0480
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505; ASTM D1928 Proc A | ||
| Vinyl Acetate Content | 18 % | 18 % | AT Plastics PTM-39 | ||
| Melt Flow | 1.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 93 | 93 | ASTM D2240 | ||
| Hardness, Shore D | 37 | 37 | ASTM D2240 | ||
| Tensile Strength at Break | 20.0 MPa | 2900 psi | Type IV (50 mm/min); ASTM D638 | ||
| Elongation at Break | 740 % | 740 % | Type IV (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 0.0480 GPa | 6.96 ksi | 1% Secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -85.0 °C | <= -121 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Process | Extrusion | ||||
| Injection Molding | |||||
| region | US & Canada | ||||