- 熔体流动速率 [g/10min]: 8.4
- 密度 [g/cm3]: 0.938
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 16.3 % | 16.3 % | AT Plastics PTM-39 |
| Melt Flow | 8.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 750 % | 750 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 63.0 °C | 145 °F | ASTM D1525 |