- 密度 [g/cm3]: 1.135
- 拉伸强度 [MPa]: 7.24
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.135 g/cc | 0.04100 lb/in³ | ASTM D1928/D 1505 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength, Yield | >= 7.24 MPa | >= 1050 psi | Heat Aging (10 days at 135°C); ASTM D638 |
| 14.5 MPa | 2100 psi | ASTM D638 | |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Tensile Set | 100 % | 100 % | Retention; ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 ohm-cm @Temperature 23.0 °C | 10.0 ohm-cm @Temperature 73.4 °F | ASTM D991 |
| 1000 ohm-cm @Temperature 90.0 °C | 1000 ohm-cm @Temperature 194 °F | ASTM D991 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 115 - 125 °C | 239 - 257 °F | |
| Drying Temperature | 70.0 °C | 158 °F | |