- 熔体流动速率 [g/10min]: 8.5
- 密度 [g/cm3]: 0.934
- 拉伸强度 [MPa]: 4.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM-D1505 |
| Vinyl Acetate Content | 15.5 % | 15.5 % | |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 91 | 91 | ASTM-D2240 |
| Hardness, Shore D | 44 | 44 | ASTM-D2240 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM-D638 |
| Tensile Strength, Yield | 4.70 MPa | 682 psi | ASTM-D638 |
| Elongation at Break | 720 % | 720 % | ASTM-D638 |
| 1% Secant Modulus | 72.0 MPa | 10400 psi | ASTM-D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | ASTM-D3418 |
| Vicat Softening Point | 62.0 °C @Load 1.02 kg | 144 °F @Load 2.25 lb | ASTM-D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 135 - 150 °C | 275 - 302 °F | Blow Film Extrusion |
| 205 - 210 °C | 401 - 410 °F | Cast Film Extrusion | |
| 225 °C | 437 °F | Extrusion Coating | |
| Die Opening | 0.0800 - 0.100 cm | 0.0315 - 0.0394 in | Blow Film Extrusion |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion |
| Roll Temperature | 25.0 °C | 77.0 °F | Chill, Cast Film Extrusion |