- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM-D1505 | ||
| Vinyl Acetate Content | 8.5 % | 8.5 % | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 93 | 93 | ASTM-D2240 | ||
| Hardness, Shore D | 45 | 45 | ASTM-D2240 | ||
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM-D638 | ||
| Film Elongation at Break, MD | 435 % | 435 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 745 % | 745 % | ASTM-D882 | ||
| Elongation at Break | 700 % | 700 % | ASTM-D638 | ||
| Secant Modulus, MD | 0.0760 GPa | 11.0 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.0790 GPa | 11.5 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 325 g | 325 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 245 g | 245 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 6.50 g/micron | 165 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 4.90 g/micron | 124 g/mil | ASTM-D1922 | ||
| Dart Drop | 4.50 g/micron | 114 g/mil | ASTM-D1709 (Method B) | ||
| Dart drop Test | 225 g | 0.496 lb | ASTM-D1709 (Method B) | ||
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 100 °C | 212 °F | ASTM-D3418 | ||
| Vicat Softening Point | 79.0 °C @Load 1.02 kg | 174 °F @Load 2.25 lb | ASTM-D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.8 % | 1.8 % | ASTM-D1003 | ||
| Gloss | 86 % | 86 % | Angle 45°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 165 - 185 °C | 329 - 365 °F | Blow Film Extrusion | ||
| Die Opening | 0.100 cm | 0.0394 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Temperature Profile (°C) | 135-185 | Blow Film Extrusion | |||