- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.934
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | D1505 | ||
| Vinyl Acetate Content | 14.5 % | 14.5 % | |||
| Thickness | 45.7 microns | 1.80 mil | Thickness Tested | ||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 675 % | 675 % | D882 | ||
| Film Elongation at Break, TD | 100 % | 100 % | D882 | ||
| Dart Drop | 8.11 g/micron | 206 g/mil | D1709 | ||
| Dart drop Test | 370 g | 0.816 lb | D1709 | ||
| Film Tensile Strength at Break, MD | 22.1 MPa | 3210 psi | D638 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | D638 | ||
| 1% Secant Modulus, MD | 50.0 MPa | 7250 psi | D882 | ||
| 1% Secant Modulus, TD | 55.2 MPa | 8010 psi | D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 90.0 °C | 194 °F | DSC Peak; D3418 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.5 % | 1.5 % | D1003 | ||
| Gloss | 87 % | 87 % | at 45; D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 193 °C | 379 °F | Blown Film | ||
| 210 °C | 410 °F | Cast Film | |||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||