- 密度 [g/cm3]: 0.94
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 17.7 - 20.3 % | 17.7 - 20.3 % | |
| Melt Index of Compound | 1.8 - 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 - 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 87 | 87 | ASTM D2240 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 750 % | 750 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.0 °C | 187 °F | ASTM D3418 |
| Vicat Softening Point | 61.0 °C | 142 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 100 - 120 °C | 212 - 248 °F | Mixture Zone |