- 熔体流动速率 [g/10min]: 8.6
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ASTM D792 |
| Melt Flow | 8.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 93.0 °C | 199 °F | DSC; ASTM D3418 |
| Vicat Softening Point | 66.0 °C | 151 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 140 °C | 284 °F | Blow Film |
| 160 °C | 320 °F | Extrusion Coating | |
| Middle Barrel Temperature | 150 °C | 302 °F | Blow Film |
| 220 °C | 428 °F | Extrusion Coating | |
| Front Barrel Temperature | 160 °C | 320 °F | Blow Film |
| 234 °C | 453 °F | Extrusion Coating | |
| Adapter Temperature | 180 °C | 356 °F | Blow Film |
| 234 °C | 453 °F | Extrusion Coating | |
| Die Temperature | 180 °C | 356 °F | Blow Film |
| 235 °C | 455 °F | Extrusion Coating | |