- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 1.30 cc-mm/m²-24hr-atm | 3.30 cc-mil/100 in²-24hr-atm | g-mm/m²-day; based on 1 mil (0.0254 mm) thick film; ASTM E96 |
| Oxygen Transmission | 197 cc-mm/m²-24hr-atm @Thickness 0.0254 mm | 500 cc-mil/100 in²-24hr-atm @Thickness 0.00100 in | Based on 1 mil (0.0254 mm) thick film; ASTM D3985 |
| Melt Flow | 2.5 g/10 min | 2.5 g/10 min | Condition not noted.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 575 % | 575 % | MD-TD Average; ASTM D882 |
| Film Elongation at Break, TD | 575 % | 575 % | MD-TD Average; ASTM D882 |
| Impact | 31.6 | 31.6 | J/mm Spencer Impact; Average of MD and TD; ASTM D3420 |
| Elmendorf Tear Strength, MD | 3.70 g/micron | 94.0 g/mil | Average of MD and TD; ASTM D1922 |
| Film Tensile Strength at Break, MD | 26.9 MPa | 3900 psi | MD-TD Average; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 71.0 °C | 160 °F | Freezing Point via DSC/ASTM D3418 |
| 92.0 °C | 198 °F | Upon Melting via DSC/ASTM D3418 | |
| Vicat Softening Point | 69.0 °C | 156 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Gloss | 109 % | 109 % | 20°; ASTM D2457 |