- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 5.5 % | 5.5 % | ExxonMobil Method | ||
| Thickness | 38.1 microns | 1.50 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 4000 ppm | 4000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.72 MPa | 1120 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.24 MPa | 1050 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 | ||
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.3 % | 7.3 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.9 % | 5.9 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 4.197 g/micron | 106.6 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 2.10 g/micron | 53.3 g/mil | ASTM D1922 | ||
| Dart Drop | 4.461 g/micron | 113.3 g/mil | ASTM D1709 | ||
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 25.1 MPa | 3640 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.9 MPa | 3470 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 127 MPa | 18400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 146 MPa | 21200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 102 °C | 216 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 89.0 °C | 192 °F | ExxonMobil Method | ||
| Vicat Softening Point | 82.8 °C | 181 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 74 % | 74 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||