- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 6.1 % | 6.1 % | ExxonMobil Method | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 6000 ppm | 6000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.76 MPa | 1270 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.45 MPa | 1080 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 | ||
| Film Elongation at Break, TD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.5 % | 7.5 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 | ||
| Dart Drop | 8.66 g/micron | 220 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 26.2 MPa | 3800 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 26.9 MPa | 3900 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 161 MPa | 23400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 102 °C | 216 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM D1003 | ||
| Gloss | 54 % | 54 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||