- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.951
- 弯曲模量 [MPa]: 0.0310
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 26.2 % | 26.2 % | ExxonMobil Method | ||
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | 190°C, 2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 28 | 28 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 9.65 MPa | 1400 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.0310 GPa | 4.50 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 21.7 J | 16.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 | ||
| 31.2 J | 23.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 75.0 °C | 167 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 48.9 °C | 120 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||