- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.928
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 0.30 g/10 min | 0.30 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.20 MPa | 1190 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.80 MPa | 986 psi | ASTM D882 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.124 GPa | 18.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.144 GPa | 20.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Dart Drop | 8.82 g/micron | 224 g/mil | F50; ASTM D1709 |
| Dart drop Test | 280 g | 0.617 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°, ASTM D-2457 |