- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.94
- 弯曲强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 0.0410
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 29 | 29 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0410 GPa | 5.95 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 648 kJ/m² | 308 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 81.0 °C | 178 °F | Exxon Method |
| Vicat Softening Point | 57.0 °C | 135 °F | 1000g; ASTM D-1525 |