- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.923
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 480 % | 480 % | ASTM D882 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Modulus of Elasticity | 0.304 GPa | 44.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Dart Drop | 5.12 g/micron | 130 g/mil | ASTM D1709 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 63 % | 63 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 204 °C | 374 - 399 °F | |