- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 9.0
- 弯曲强度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Modulus of Elasticity | 0.207 GPa | 30.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.117 GPa | 17.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.138 GPa | 20.0 ksi | ASTM D882 |
| Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
| Dart drop Test | 200 g | 0.441 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 73 % | 73 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 193 °C | 360 - 379 °F | |