- 熔体流动速率 [g/10min]: 0.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ISO 1183 |
| Vinyl Acetate Content | 14 % | 14 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 30.0 - 300 microns | 1.18 - 11.8 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.50 MPa | 943 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 5.00 MPa | 725 psi | ISO 527-3 |
| Film Elongation at Break, MD | 320 % | 320 % | ISO 527-3 |
| Film Elongation at Break, TD | 610 % | 610 % | ISO 527-3 |
| Modulus of Elasticity | 0.0650 GPa | 9.43 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 1.80 g/micron | 45.7 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 3.10 g/micron | 78.7 g/mil | ISO 6383-2 |
| Dart drop Test | 600 g | 1.32 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 36.0 MPa | 5220 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 91.0 °C | 196 °F | ISO 11357 |
| Vicat Softening Point | 72.0 °C | 162 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.5 % | 2.5 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | |