- 熔体流动速率 [g/10min]: 8.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Methyl Acrylate Content | 9.0 % | 9.0 % | |||
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 400 % | 400 % | |||
| Film Elongation at Break, TD | 800 % | 800 % | |||
| Dart Drop | 6.69 g/micron | 170 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.6 MPa | 4000 psi | ASTM D638 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D638 | ||
| 1% Secant Modulus, MD | 89.6 MPa | 13000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 110 MPa | 16000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.7 % | 2.7 % | ASTM D1003 | ||
| Gloss | 80 % | 80 % | at 45° | ||
| Descriptive Properties | |||||
| process | Extrusion | ||||
| Film | |||||
| region | US & Canada | ||||