- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 2.0
- 拉伸强度 [MPa]: 45.0
- 热变形温度 [℃]: 93.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Water Absorption | 2.0 % | 2.0 % | |
| Moisture Absorption at Equilibrium | 0.36 % | 0.36 % | Humidity Absorption |
| Melt Flow | 0.80 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.80 g/10 min @Load 8.38 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min |
| Elongation at Break | 40 % | 40 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | |
| 3.9 @Frequency 100 Hz | 3.9 @Frequency 100 Hz | ||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | |
| 0.050 @Frequency 100 Hz | 0.050 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | |
| Vicat Softening Point | 93.0 °C | 199 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |