- 熔体流动速率 [g/10min]: 13.3
- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 1.8
- 拉伸强度 [MPa]: 80.0
- 热变形温度 [℃]: 82.0
- 透光率 [%]: 80.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.18 g/cc | 0.0426 lb/in³ | |
Water Absorption | 1.8 % | 1.8 % | |
Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | Humidity Absorption |
Melt Flow | 13.3 g/10 min @Load 3.80 kg, Temperature 230 °C | 13.3 g/10 min @Load 8.38 lb, Temperature 446 °F | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min |
Elongation at Break | 5.0 % | 5.0 % | Nominal Strain; 50 mm/min |
Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min |
Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | |
Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | |
Tensile Creep Modulus, 1 hour | 2600 MPa | 377000 psi | |
Tensile Creep Modulus, 1000 hours | 1600 MPa | 232000 psi | |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | |
3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ||
Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | |
0.050 @Frequency 100 Hz | 0.050 @Frequency 100 Hz | ||
Comparative Tracking Index | 600 V | 600 V | |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 20.0 °C | 38.9 µin/in-°F @Temperature 68.0 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | |
Vicat Softening Point | 84.0 °C | 183 °F | 50°C/hr; 50N |
Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
Optical Properties | Metric | English | Comments |
Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |