- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 0.16
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 8.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| Tensile Modulus | 2.90 GPa | 420 ksi | ASTM D638 |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 |
| Gardner Impact | 0.226 J | 0.167 ft-lb | Falling Weight; ASTM D3029GB |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Vicat Softening Point | 102 °C | 215 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 92 % | 92 % | Luminous Transmittance; ASTM D1003 |