- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.07
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 43.0
- 弯曲模量 [MPa]: 1.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C | 6.0 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D 1238 |
| 38 g/10 min @Load 21.6 kg, Temperature 220 °C | 38 g/10 min @Load 47.6 lb, Temperature 428 °F | ASTM D 1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D 638 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ASTM D 638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D 638 |
| Tensile Modulus | 1.95 GPa | 283 ksi | ASTM D 638 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C | 1.12 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C @Load 5.10 kg | 194 °F @Load 11.2 lb | 120°C/hr; ASTM D 1525 |
| 102 °C @Load 1.02 kg | 216 °F @Load 2.25 lb | 120°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Dry Time | 2.00 - 4.00 hour @Temperature 80.0 °C | 2.00 - 4.00 hour @Temperature 176 °F | |