- 熔体流动速率 [g/10min]: 5.5
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.481
- 弯曲模量 [MPa]: 1.58
- 热变形温度 [℃]: 78.0
- 透光率 [%]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.5 g/10 min @Load 11.0 lb, Temperature 392 °F | Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength at Break | 25.5 MPa | 3700 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 52 % | 52 % | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.58 GPa | 229 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.6 % | 2.6 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |