- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.196
- 断裂伸长率 [%]: 98.04
- 弯曲模量 [MPa]: 3.040
- 透光率 [%]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 3.80 kg, Temperature 230 °C | 14 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 65.7 MPa | 9530 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Modulus of Elasticity | 3.23 GPa | 469 ksi | ASTM D638 |
| Flexural Yield Strength | 98.04 MPa | 14220 psi | ASTM D790 |
| Flexural Modulus | 3.040 GPa | 440.9 ksi | ASTM D790 |
| Compressive Yield Strength | 97.9 MPa | 14200 psi | ASTM D695 |
| Izod Impact, Notched | 0.196 J/cm | 0.368 ft-lb/in | 0.250 inches; ASTM D256 |
| Impact | 115 | 115 | cm Falling Ball Impact |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 59.9 µm/m-°C @Temperature 20.0 °C | 33.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.46 J/g-°C | 0.349 BTU/lb-°F | |
| Thermal Conductivity | 0.209 W/m-K | 1.45 BTU-in/hr-ft²-°F | ASTM D177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.00 °C | 181.4 °F | ASTM D648 |
| Vicat Softening Point | 98.00 °C | 208.4 °F | ASTM D1525; 1 kg |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Transmission, Visible | 93 % @Thickness 3.20 mm | 93 % @Thickness 0.126 in | ASTM D1003 |