- 熔体流动速率 [g/10min]: 0.791
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 42.0
- 热变形温度 [℃]: 92.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | 23°C, 50%; ISO 62 |
| Water Absorption at Saturation | 1.5 % | 1.5 % | Immersion; ISO 62 |
| Melt Flow | 0.791 g/10 min @Load 3.80 kg, Temperature 230 °C | 0.791 g/10 min @Load 8.38 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min; ISO 527 |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature 0.000 - 50.0 °C | 66.7 µin/in-°F @Temperature 32.0 - 122 °F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Vicat Softening Point | 94.0 °C | 201 °F | B50; ISO 306 |
| Glass Transition Temp, Tg | 115 °C | 239 °F | ISO 11357 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 707 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Transmission, Visible | 90 % | 90 % | Transmission Factor; DIN 5036 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 240 °C | 446 - 464 °F | Cylinder/Barrel Temperature |
| Melt Temperature | 230 - 240 °C | 446 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | <= 85.0 °C | <= 185 °F | Predrying |
| Dry Time | 2 - 3 hour | 2 - 3 hour | Desiccant-type drier |