- 熔体流动速率 [g/10min]: 2.0
- 缺口冲击强度: 0.422
- 拉伸强度 [MPa]: 71.7
- 断裂伸长率 [%]: 120
- 透光率 [%]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C | 2.0 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 71.7 MPa | 10400 psi | ASTM D638 |
| Elongation at Yield | 13 % | 13 % | ASTM D638 |
| Tensile Modulus | 3.17 GPa | 460 ksi | ASTM D638 |
| Flexural Yield Strength | 120 MPa | 17400 psi | ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm @Thickness 3.17 mm, Temperature 22.8 °C | 0.790 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.17 mm | 219 °F @Thickness 0.125 in | annealed; ASTM D648 |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 93 % | 93 % | Total light Transmission; ASTM D1003 |