- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.147
- 弯曲模量 [MPa]: 3.275
- 透光率 [%]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Index of Compound | 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C | 1.7 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 13 % | 13 % | ASTM D638 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 3.275 GPa | 475.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.147 J/cm | 0.275 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 60 Hz | 4.0 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | 4kV/s; ASTM D149 |
| Dissipation Factor | 0.050 @Frequency 60 Hz | 0.050 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C | 33.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | 1 kg; ASTM D1525 |
| Annealing Point | 80.0 - 90.0 °C | 176 - 194 °F | 3-5 hours |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 0.50 % @Thickness 3.20 mm | 0.50 % @Thickness 0.126 in | ASTM D1003 |
| Transmission, Visible | 93 % @Thickness 3.20 mm | 93 % @Thickness 0.126 in | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | Injection molding cylinder temperature |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Injection Pressure | 78.45 - 147.1 MPa | 11380 - 21340 psi | |