- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.2
- 弯曲强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 3.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 101 | 101 | ISO 2039-2 |
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Flexural Strength | 107 MPa | 15500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.03 GPa | 439 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 78.0 µm/m-°C @Temperature 20.0 °C | 43.3 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Vicat Softening Point | >= 105 °C | >= 221 °F | ISO 306A |
| Flammability, UL94 | HB | HB | |
| Flammability Test | 4.0 | 4.0 | BS 476, Pt7 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489/A |
| Transmission, Visible | >= 92 % | >= 92 % | clear grade; in 3 mm (colored grades lower); ASTM D1003 |