- 熔体流动速率 [g/10min]: 5.8
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.3
- 缺口冲击强度: 1.4
- 弯曲模量 [MPa]: 3.10
- 热变形温度 [℃]: 99.0
- 透光率 [%]: 80.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89 | 89 | ISO 2039-2 |
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 52.0 MPa | 7540 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Flexural Strength | 88.0 MPa | 12800 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.40 kJ/m² | 0.666 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.180 J/cm² | 0.857 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75A |
| Vicat Softening Point | 100 °C | 212 °F | ISO 306B |
| 106 °C | 223 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Haze | 97.5 % | 97.5 % | ASTM D1003 |
| Transmission, Visible | 80.5 % | 80.5 % | ASTM D1003 |