- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 0.3
- 缺口冲击强度: 16.0
- 弯曲模量 [MPa]: 2.90
- 热变形温度 [℃]: 99.0
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 15 g/10 min | 15 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 97 | 97 | ISO 2039-2 |
| Tensile Strength | 61.0 MPa | 8850 psi | ISO 527 |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527 |
| Flexural Strength | 59.0 MPa | 8560 psi | ISO 178 |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75A |
| Vicat Softening Point | 100 °C | 212 °F | ISO 306B |
| 104 °C | 219 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |