- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.4
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 1.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 74 | 74 | ISO 2039-2 |
| Tensile Strength | 29.0 MPa | 4210 psi | ISO 527 |
| Elongation at Break | 27 % | 27 % | ISO 527 |
| Flexural Strength | 42.0 MPa | 6090 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 5.30 J/cm² | 25.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.530 J/cm² | 2.52 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75A |
| Vicat Softening Point | 69.0 °C | 156 °F | ISO 306B |
| 84.0 °C | 183 °F | ISO 306A | |