- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | ASTM D570 |
| Linear Mold Shrinkage | <= 0.025 cm/cm | <= 0.025 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 Procedure A |
| Tensile Strength | 62.0 - 69.0 MPa | 8990 - 10000 psi | specimen type 1, 5 mm/mn; ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | |
| Modulus of Elasticity | 3.172 GPa | 460.1 ksi | |
| Flexural Strength | 110.3 MPa | 16000 psi | ASTM D790 (Method 1, Procedure A) |
| Compressive Yield Strength | 111 MPa | 16100 psi | ASTM D695 |
| Shear Strength | 59.6 MPa | 8640 psi | |
| Izod Impact, Notched | 0.160 J/cm | 0.300 ft-lb/in | ASTM D256 method C |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | <= 1.00e+14 ohm @Temperature 28.0 °C | <= 1.00e+14 ohm @Temperature 82.4 °F | 75% RH; ASTM D257 |
| Dielectric Constant | 3.0 @# of Cycles 1000 | 3.0 @# of Cycles 1000 | ASTM D150 |
| 3.0 @# of Cycles 1.00e+6 | 3.0 @# of Cycles 1.00e+6 | ASTM D150 | |
| 4.0 @# of Cycles 60.0 | 4.0 @# of Cycles 60.0 | ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | short time test; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Specific Heat Capacity | 1.47 J/g-°C | 0.351 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.209 W/m-K | 1.45 BTU-in/hr-ft²-°F | ASTM C177-76 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 190 °C | 338 - 374 °F | thermoforming temperature |