- 熔体流动速率 [g/10min]: 5.9
- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.3
- 缺口冲击强度: 3.2
- 弯曲模量 [MPa]: 2.20
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | |
| Melt Flow | 5.9 g/10 min | 5.9 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45 | 45 | ISO 2039-2 |
| Tensile Strength | 52.0 MPa | 7540 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.20 kJ/m² | 1.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.320 J/cm² | 1.52 ft-lb/in² | ISO 179/1eA |
| 3.60 J/cm² | 17.1 ft-lb/in² | ISO 179/1eU | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 103 µm/m-°C | 57.2 µin/in-°F | ASTM E831 |
| Vicat Softening Point | 89.0 °C | 192 °F | ISO 306B |
| 96.0 °C | 205 °F | ISO 306A | |
| Heat Distortion Temperature | 83.0 °C | 181 °F | ISO 75A |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 2.5 % | 2.5 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |