Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer

Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer 物性表: Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer物性表及特性介绍,Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer注塑参数详情,如需Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 5.0
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 1.6
  • 拉伸强度 [MPa]: 30.0
  • 弯曲模量 [MPa]: 1.97
  • 硬度: 61.0
  • 透光率 [%]: 89.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.05 g/cc1.05 g/ccASTM D792
Water Absorption 0.10 %0.10 %24 hr; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm0.0020 - 0.0060 in/inASTM D955
Melt Flow 5.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C
5.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F
Condition G; ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 6161ASTM D785
Tensile Strength, Yield 30.0 MPa4350 psiASTM D638
Elongation at Break 52 %52 %ASTM D638
Tensile Modulus 2.10 GPa305 ksiASTM D638
Flexural Strength 46.0 MPa6670 psiASTM D790
Flexural Modulus 1.97 GPa286 ksiASTM D790
Izod Impact, Notched 1.60 J/cm3.00 ft-lb/inreverse notched; ASTM D256
Izod Impact, Unnotched 2.20 J/cm4.12 ft-lb/inASTM D256
Gardner Impact 2.00 J1.48 ft-lbGeometry GB; ASTM D5420
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C189 °FASTM D648
Vicat Softening Point 99.0 °C210 °FASTM D1525
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.561.56nD; ASTM D542
Haze 1.8 %1.8 %ASTM D1003
Transmission, Visible 89 %89 %ASTM D1003
 
Processing PropertiesMetricEnglishComments
Rear Barrel Temperature 179 - 213 °C354 - 415 °F
Middle Barrel Temperature 185 - 218 °C365 - 424 °F
Front Barrel Temperature 191 - 224 °C376 - 435 °F
Melt Temperature 204 - 238 °C399 - 460 °F
Mold Temperature 27.0 - 54.0 °C80.6 - 129 °F
Back Pressure 0.689 MPa100 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-30386.html

免责声明: 本文 Ineos Nova Zylar® 530 Clear Impact Modified Acrylic Copolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4